Journal of Inorganic Materials, Volume. 39, Issue 7, 793(2024)

Influence of RE-Si-Al-O Glass Phase on Microstructure and CMAS Corrosion Resistance of High Entropy Rare Earth Disilicates

Liuyuan LI*... Kaiming HUANG, Xiuyi ZHAO, Huichao LIU and Chao WANG |Show fewer author(s)
Figures & Tables(13)
XRD patterns of (4RE0.25)2Si2O7 ceramics and (4RE0.25)2Si2O7/RE-Si-Al-O multiphase ceramics
SEM images and EDS mappings of (4RE0.25)2Si2O7 ceramics and (4RE0.25)2Si2O7/RE-Si-Al-O multiphase ceramics
EDS patterns of glass phases in (4RE0.25)2Si2O7/RE-Si-Al-O multiphase ceramics
Cross-sectional SEM images of (4RE0.25)2Si2O7 ceramics and (4RE0.25)2Si2O7/RE-Si-Al-O multiphase ceramics after corrosion at 1300 ℃ for 48 h
XRD patterns of (4RE0.25)2Si2O7 and RE-Si-Al-O mixed with CMAS after calcination at 1300 ℃ for 48 h
XRD patterns of (4RE0.25)2Si2O7 ceramics and (4RE0.25)2Si2O7/RE-Si-Al-O multiphase ceramics after corrosion at 1500 ℃ for (a) 24 and (b) 48 h
Cross-sectional SEM images of (4RE0.25)2Si2O7 ceramics after corrosion at 1500 ℃ for (a) 24 and (b) 48 h (c) Partial enlargement of area in (b)
Cross-sectional SEM images of (4RE0.25)2Si2O7/RE-Si-Al-O multiphase ceramics after corrosion at 1500 ℃ for 24 and 48 h
Local enlarged SEM images of (4RE0.25)2Si2O7/RE-Si-Al-O multiphase ceramics after corrosion at 1500 ℃ for 48 h
  • Table 1. Elemental composition of each point in Fig. 2 (%, in atom)

    View table
    View in Article

    Table 1. Elemental composition of each point in Fig. 2 (%, in atom)

    SpotYYbErTmSiOMatter
    14.543.553.493.4019.2965.73(4RE0.25)2Si2O7
    24.424.315.484.0918.9962.71(4RE0.25)2Si2O7
    34.494.194.234.0619.2763.76(4RE0.25)2Si2O7
    45.185.695.485.3021.4156.94(4RE0.25)2Si2O7
    54.261.842.132.1117.5172.15(4RE0.25)2Si2O7
  • Table 2. Elemental composition of each point in Fig. 4 (%, in atom)

    View table
    View in Article

    Table 2. Elemental composition of each point in Fig. 4 (%, in atom)

    SpotYbTmErYSiOCaMgAlSmLaMatter
    10.760.690.710.6922.1557.649.430.996.94CMAS
    22.852.782.672.1921.1652.9413.052.36Ca2RE8(SiO4)6O2
    36.065.555.233.8121.7557.60(4RE0.25)2Si2O7
    41.911.892.021.2423.5558.2111.18CMAS
    50.610.540.540.4623.4358.288.820.906.42CMAS
    62.021.821.840.8224.3957.8411.27Ca2RE8(SiO4)6O2
    75.545.115.363.7722.7457.48(4RE0.25)2Si2O7
    80.530.610.690.5323.8258.489.715.63Yb-Si-Al-O-Ca
    90.510.400.520.4322.4059.878.460.756.66CMAS
    101.791.901.980.9523.7258.8510.81Ca2RE8(SiO4)6O2
    115.984.924.893.5621.6858.97(4RE0.25)2Si2O7
    120.370.340.370.2323.1459.048.500.277.74Y-Si-Al-O-Ca
    130.760.710.680.6924.7555.799.231.016.220.16CMAS
    141.871.992.070.8026.0954.9712.020.19Ca2RE8(SiO4)6O2
    155.985.965.543.0223.8155.69(4RE0.25)2Si2O7
    160.220.350.450.2126.2657.497.130.286.321.29La-Si-Al-O-Ca
  • Table 3. Elemental composition of each point in Fig. 7 (%, in atom)

    View table
    View in Article

    Table 3. Elemental composition of each point in Fig. 7 (%, in atom)

    SpotYbTmErYSiOCaMgAlLaMatter
    11.391.121.030.8422.2654.2114.350.394.41CMAS
    27.808.128.218.4614.5745.437.41Ca2RE8(SiO4)6O2
    38.108.398.134.0328.6842.67(4RE0.25)2Si2O7
  • Table 4. Elemental composition of each point in Fig. 9 (%, in atom)

    View table
    View in Article

    Table 4. Elemental composition of each point in Fig. 9 (%, in atom)

    SpotYbTmErYSiOCaMgAlLaMatter
    11.230.900.840.7223.0155.9210.200.386.80CMAS
    26.177.437.758.0216.4747.836.33Ca2RE8(SiO4)6O2
    36.926.616.343.6424.7351.76(4RE0.25)2Si2O7
    40.340.440.480.2125.8954.5910.730.346.98Yb-Si-Al-O-Ca
    51.010.920.810.7424.1055.699.650.226.86CMAS
    65.926.236.526.9416.8552.315.23Ca2RE8(SiO4)6O2
    75.275.355.643.7723.1156.86(4RE0.25)2Si2O7
    80.640.690.760.4124.0356.459.700.436.89Y-Si-Al-O-Ca
    95.615.826.156.4315.9753.995.021.01Ca2RE8(SiO4)6O2
    105.815.345.623.5023.4756.26(4RE0.25)2Si2O7
    110.390.470.530.2325.1156.149.010.277.180.67La-Si-Al-O-Ca
    121.731.821.891.5728.5454.010.368.171.91La-Si-Al-O
Tools

Get Citation

Copy Citation Text

Liuyuan LI, Kaiming HUANG, Xiuyi ZHAO, Huichao LIU, Chao WANG. Influence of RE-Si-Al-O Glass Phase on Microstructure and CMAS Corrosion Resistance of High Entropy Rare Earth Disilicates[J]. Journal of Inorganic Materials, 2024, 39(7): 793

Download Citation

EndNote(RIS)BibTexPlain Text
Save article for my favorites
Paper Information

Category:

Received: Jan. 30, 2024

Accepted: --

Published Online: Aug. 30, 2024

The Author Email: LI Liuyuan (liuyuanwuming@163.com)

DOI:10.15541/jim20240018

Topics