Laser & Optoelectronics Progress, Volume. 56, Issue 24, 241403(2019)
Effect of Laser Power on Corrosion Resistance of 42CrMo Cladding Stellite-6 Coating
Fig. 1. Corrosion rate of substrate and Stellite-6 coating prepared at different laser powers in NaCl solution
Fig. 2. Dynamic polarization in NaCl solution of base steel and Stellite-6 coating samples prepared at different laser powers
Fig. 3. Polarization resistance curves of base steel and Stellite-6 coating prepared at different laser powers in NaCl solution
Fig. 4. Corrosion morphologies of base steel and Stellite-6 coating prepared at different powers after soaking in NaCl solution for 24 h. (a) Base steel; (b) 1500 W; (c)2000 W; (d) 2500 W; (e) 3000 W
Fig. 5. Metallographic structures of the molten pool in cladding layer prepared at different laser powers. (a) 1500 W; (b) 2000 W; (c) 2500 W; (d) 3000 W
|
|
|
Get Citation
Copy Citation Text
Chen Cui, Meiping Wu, Wei Cheng. Effect of Laser Power on Corrosion Resistance of 42CrMo Cladding Stellite-6 Coating[J]. Laser & Optoelectronics Progress, 2019, 56(24): 241403
Category: Lasers and Laser Optics
Received: Apr. 18, 2019
Accepted: Jun. 5, 2019
Published Online: Nov. 26, 2019
The Author Email: Wu Meiping (wmp169@jiangnan.edu.cn)