Journal of Inorganic Materials, Volume. 35, Issue 2, 211(2020)
Figures & Tables(12)
2. Diagram of deformation compatibility of phase change of the NiS particle
3. Schematic diagram of stress distribution around the NiS particle
4. Schematic diagram of circumferential stress gradient around the NiS particle
5. Schematic diagram of tempered stress along the thickness direction of the tempered glass
6. Relationship between the circumferential stress and diameter of the NiS particle
7. Schematic diagram of local strength along the thickness direction of the tempered glass with thickness of 6 mm and surface stress of 90 Mpa
8. Relationship between diameter distribution and its proportion for NiS (statistical by on-site detection data)
9. Relationship between circumferential stress and service ambient temperature
Table 1. Values of calculating parameters[3]
View tableView in ArticleTable 1. Values of calculating parameters[3]
Calculating parameter Value $E_{1}$/GPa 70 $E_{2}$/GPa 70 $\mu_{1}$ 0.24 $\mu_{2}$ 0.27 $\alpha_{1}$ 8.8×10-6 $\alpha_{2}$ 16.3×10-6 $\phi$/% 3 $\sigma{i}$/MPa 160
Table 2. Average circumferential stress with various diameters of the NiS particles
View tableView in ArticleTable 2. Average circumferential stress with various diameters of the NiS particles
Diameter/mm Stress/MPa Diameter/mm Stress/MPa 0.02 30.3 0.20 136.7 0.05 64.8 0.30 154.1 0.06 73.7 0.40 164.9 0.07 81.7 0.50 171.7 0.08 88.9 0.60 176.5 0.10 100.8 0.70 180.4 0.12 110.8 0.80 183.3 0.14 118.9 0.90 185.5 0.16 125.9 1.0 187.1 0.18 131.7 2.0 196.2
Table 3. Local strength at the neutral layer with different surface stress of the tempered glass/Mpa
View tableView in ArticleTable 3. Local strength at the neutral layer with different surface stress of the tempered glass/Mpa
Surface stress 40 50 60 70 80 90 Local strength 144 140 136 132 128 124 Surface stress 100 110 120 130 140 150 Local strength 120 116 112 108 104 100
Tools
Get Citation
Copy Citation Text
Xiao-Gen LIU, Yi-Wang BAO, De-Tian WAN, Yu-Kang SUN.
Paper Information
Category: RESEARCH PAPER
Received: Feb. 25, 2018
Accepted: --
Published Online: Jan. 27, 2021
The Author Email:
© Copyright 2018-2021 | Chinese Laser Press.
All Rights Reserved 沪ICP备15018463号-20