Journal of Inorganic Materials, Volume. 35, Issue 12, 1385(2020)

Stable Zirconium Carbide Fibers Fabricated by Centrifugal Spinning Technique

Bowen CHEN1...2,3, Jingxiao WANG1,2, Youlin JIANG1,2,3, Haijun ZHOU1,2, Chunjing LIAO1,2, Xiangyu ZHANG1,2, Yanmei KAN1,2, and Dewei NI12,* |Show fewer author(s)
Author Affiliations
  • 1State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China
  • 2Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China
  • 3University of Chinese Academy of Sciences, Beijing 100049, China
  • show less
    Figures & Tables(6)
    Schematic of the centrifugal spinning system and the preparation of ZrC fibers
    FT-IR spectra of ZrC precursors with different ZrO(CH3COO)2 : C12H22O11 ratios: (a) 4 : 1; (b) 4 : 1.2; (c) 4 : 1.5; and (d) ZrC precursor (with ZrO(CH3COO)2 : C12H22O11= 4 : 1.5) after pyrolysis at 600 ℃
    TG-DSC curves of the as-spun green fibers prepared from ZrC precursor with ZrO(CH3COO)2 : C12H22O11=4 : 1.5
    XRD patterns of ZrC fibers prepared from ZrC precursors with different ZrO(CH3COO)2:C12H22O11 ratios after heat- treatment at temperature range from 1400 to 1600 ℃ for 2 h(a) 4 : 1.5 @1400 ℃; (b) 4 : 1.5 @1500 ℃; (c) 4 : 1.5 @1600 ℃; (d) 4 : 1.2 @1600 ℃; (e) 4 : 1 @1600 ℃
    SEM images of ZrC fibers prepared from ZrC precursor with ZrO(CH3COO)2 : C12H22O11=4 : 1.5((a) as-spun green fibers; (b) after heat-treatment at 600 ℃ and (c) after heat- treatment at 1600 ℃); and (d) TEM image of ZrC fibers after heat-treatment at 1600 ℃The insets in (a,b,c) are the corresponding local enlarged images; while the inset in (d) is the selected area electron diffraction (SAED) pattern of ZrC fibers
    SEM images of ZrC fibers prepared from ZrC precursors with different ZrO(CH3COO)2 : C12H22O11 ratios after heat-treatment at 2000 ℃ for 2 h(a, b) 4 : 1; (c, d) 4 : 1.2; (e, f) 4 : 1.5
    Tools

    Get Citation

    Copy Citation Text

    Bowen CHEN, Jingxiao WANG, Youlin JIANG, Haijun ZHOU, Chunjing LIAO, Xiangyu ZHANG, Yanmei KAN, Dewei NI. Stable Zirconium Carbide Fibers Fabricated by Centrifugal Spinning Technique[J]. Journal of Inorganic Materials, 2020, 35(12): 1385

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: RESEARCH LETTERS

    Received: Jan. 13, 2020

    Accepted: --

    Published Online: Mar. 10, 2021

    The Author Email: NI Dewei (deweini@mail.sic.ac.cn)

    DOI:10.15541/jim20200031

    Topics