Journal of Inorganic Materials, Volume. 36, Issue 10, 1111(2021)

Influence of SiC Nanowires on the Damage Evolution of SiCf/SiC Composites

Longbin LI1...2, Yudong XUE1,2, Jianbao HU1,2, Jinshan YANG1,2, Xiangyu ZHANG1,2, and Shaoming DONG12,* |Show fewer author(s)
Author Affiliations
  • 11. State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China
  • 22. Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing 100049, China
  • show less
    Figures & Tables(10)
    Schematic figure of three-point test within-situ AE monitoring system
    Typical SEM images of (a, b) as-grown SiCnw, (c) BN-coated SiCnw, and typical SEM images demonstrating the pore size of (d) SiCf/SiC and (e) SiCf/SiC-SiCnw composites
    SEM fractural morphologies of (a) as-grown SiCnw, (b, c) BN-coated SiCnw in composites Local parts marked by white rectangular borders demonstrating that SiCnw tends to break (a) or pull out (b, c)
    Fracture morphologies of composite (a) SiCf/SiC, (b) SiCf/SiC-SiCnw and (c) SiCf/SiC-SiCnw/BN The images demonstrating the pull-out length of fibers
    Representative normalized cumulative AE energy curves as a function of stress (a) for composite SiCf/SiC (orange), SiCf/SiC-SiCnw (black) and SiCf/SiC-SiCnw/BN (blue)
    Typical stress-strain curves of SiCf/SiC(orange), SiCf/SiC-SiCnw (black) and SiCf/SiC-SiCnw/BN (blue)
    Scatter diagrams of the energy of individual AE events as a function of time in composites (a) SiCf/SiC, (b) SiCf/SiC-SiCnw, and (c) SiCf/SiC-SiCnw/BN
    SEM micrographs of crack propagation around the indentation in composites (a) SiCf/SiC; (b) SiCf/SiC-SiCnw; (c) SiCf/SiC-SiCnw/BN
    • Table 1.

      Density and porosity of different composites

      View table
      View in Article

      Table 1.

      Density and porosity of different composites

      CompositeSiCf/SiC SiCf/SiC- SiCnw/BN SiCf/ SiC-SiCnw
      Bulk density/(g·cm-3) (1.98±0.03)(2.02±0.04)(2.08±0.03)
      Open porosity/%(17.64±1.08)(14.39±0.60)(11.58±1.35)
    • Table 2.

      Properties of original composites, as-grown and BN-coated hierarchical composites

      View table
      View in Article

      Table 2.

      Properties of original composites, as-grown and BN-coated hierarchical composites

      CompositeSiCnw content / wt% Flexural strength, σu/MPa Proportional limit stress, σPL/MPa Strain at flexural strength, εu/% First AE stress, σmin/MPa AE onset stress, σonset/MPa
      SiCf/SiC 0(356.7±16.2)(153.9±6.4)(0.39±0.05)(58.8±7.5)(116.1±8.9)
      SiCf/SiC-SiCnw2.0(412.6±22.4)(185.1±7.7)(0.63±0.06)(66.1±6.2)(155.8±7.7)
      SiCf/SiC-SiCnw/BN 2.0(506.4±28.3)(247.7±8.6)(0.88±0.12)(78.5±5.2)(171.6±15.9)
    Tools

    Get Citation

    Copy Citation Text

    Longbin LI, Yudong XUE, Jianbao HU, Jinshan YANG, Xiangyu ZHANG, Shaoming DONG. Influence of SiC Nanowires on the Damage Evolution of SiCf/SiC Composites [J]. Journal of Inorganic Materials, 2021, 36(10): 1111

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: RESEARCH LETTER

    Received: Jan. 27, 2021

    Accepted: --

    Published Online: Nov. 26, 2021

    The Author Email: DONG Shaoming (smdong@mail.sic.ac.cn)

    DOI:10.15541/jim20210045

    Topics