Acta Optica Sinica, Volume. 40, Issue 6, 0614002(2020)

Effect of Laser Remelting on Properties of Mg-Zn-Y-Zr Alloy at Different Powers

Yueyang Liu, Shiyou Gao*, Yingcai Zhou, Di Liu, and Yanan Wei
Author Affiliations
  • College of Mechanical Engineering, Yanshan University, Qinhuangdao, Hebei 066004, China
  • show less
    Figures & Tables(15)
    XRD patterns of Mg-Zn-Y-Zr alloy solidified under different laser powers
    (a) EDS analysis positions of substrate organization; (b)-(d) analysis results of micro segregation in different positions
    Microstructure and area classification of longitudinal section under different laser powers. (a) 800 W; (b) 1000 W; (c) 1200 W; (d) 2000 W
    Optical micrograph of FGR. (a) 800 W; (b) 1000 W; (c) 1200 W; (d) 2000 W
    Microstructure in FGR and EDS analysis positions of substrate organization under different laser powers. (a) 800 W; (b) 1000 W; (c) 1200 W; (d) 2000 W
    Heat affected zone and fine grain zone hardness distribution characteristics. (a) 800 W; (b) 1000 W; (c) 1200 W; (d) 2000 W
    Vickers hardness-crystal zone curve. (a) 800 W; (b) 1000 W; (c) 1200 W; (d) 2000 W
    Curves of Vickers hardness and laser power
    Curve of friction coefficients and time. (a) 800 W; (b) 1000 W; (c) 1200 W; (d) 2000 W
    Comparison chart of weight loss
    SEM morphology of worn surface on remelting layer. (a) 800 W; (b) 1000 W; (c) 1200 W; (d) 2000 W
    • Table 1. Machining parameters of laser remelting

      View table

      Table 1. Machining parameters of laser remelting

      Serial numberLaser power P /kWScanning speed V /(mm·s-1)Spot diameter D /mmLap rate η /%
      A10.830350
      A21.030350
      A31.230350
      A42.030350
    • Table 2. XRD analysis of the alloy solidified under different laser powers

      View table

      Table 2. XRD analysis of the alloy solidified under different laser powers

      Laser power /W(102)α(110)αLattice constant
      2θ /(°)d /nm2θ /(°)d /nma /nmc /nmc/a
      80047.8701.898657.4431.60293.20585.20461.623494915
      100047.9171.896957.4621.60243.20485.19701.621630055
      120047.9191.896857.4441.60293.20585.19531.620593924
      200047.9611.895357.5191.60103.20195.19291.621818295
    • Table 3. Analysis results of EDS in second-phase(atomic fraction, %)

      View table

      Table 3. Analysis results of EDS in second-phase(atomic fraction, %)

      ElementABCDEFGH
      Mg81.6797.3788.0495.8578.4995.0167.1594.78
      Zn14.661.849.753.1117.374.2927.104.13
      Y2.990.321.630.513.620.704.830.71
      Zr0.680.470.580.530.520.000.920.38
      Zn/Y4.905.755.986.104.796.135.615.82
    • Table 4. Mean value of friction coefficient in the stage of wear stability

      View table

      Table 4. Mean value of friction coefficient in the stage of wear stability

      Laser power /WMean value of friction coefficient
      8002.234
      10001.873
      12001.493
      20001.174
    Tools

    Get Citation

    Copy Citation Text

    Yueyang Liu, Shiyou Gao, Yingcai Zhou, Di Liu, Yanan Wei. Effect of Laser Remelting on Properties of Mg-Zn-Y-Zr Alloy at Different Powers[J]. Acta Optica Sinica, 2020, 40(6): 0614002

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: Lasers and Laser Optics

    Received: Dec. 2, 2019

    Accepted: Dec. 5, 2019

    Published Online: Mar. 6, 2020

    The Author Email: Gao Shiyou (gao58@sina.com)

    DOI:10.3788/AOS202040.0614002

    Topics