Preparation of Silicon Nitride with High Thermal Conductivity and High Flexural Strength Using YbH2-MgO as Sintering Additive

Weide WANG1...2, Huanbei CHEN3, Shishuai LI1,2, Dongxu YAO1,*, Kaihui ZUO1 and Yuping ZENG1 |Show fewer author(s)
Author Affiliations
  • 11. Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China
  • 22. University of Chinese Academy of Sciences, Beijing 100049, China
  • 33. Nanjing Electronic Devices Institute, Nanjing 210016, China
  • show less
    Figures & Tables(9)
    (a) Elemental distributions of YbHM after ball milling, (b) XRD patterns of α-Si3N4 raw powder, YbHM after ball milling, and YbHM after pre-sintering, (c) elemental distributions of YbHM after pre-sintering
    XRD patterns of powder mixture of YbH2 and SiO2 with moler ratio of 1 : 1 before and after pre-sintering
    (a) In-situ observation of shrinkage behaviors of the Si3N4 ceramics, (b) relative density after gas-pressure sintering, and (c) weight loss after gas-pressure sintering
    XRD patterns of Si3N4 samples after being sintered at 1900 ℃ for 4 and 24 h
    Elemental distributions of sample YbHM after being sintered at 1900 ℃ for 12 h
    SEM images of the polished surfaces
    EDS analysis of the intergranular phases in YbOM and YbHM specimens
    (a) Thermal conductivities and (b) flexural strengths of Si3N4 samples after gas pressure sintering
    • Table 1. Thermal conductivities of Si3N4 doped with different rare-earth hydride

      View table
      View in Article

      Table 1. Thermal conductivities of Si3N4 doped with different rare-earth hydride

      AdditiveIonic radius /nmAnnealing time at 1900 ℃/hThermal conductivity /(W·m-1·K-1)
      GdH2[25]0.0944 h98.07
      12 h119.07
      24 h134.90
      YH2[23]0.0894 h101.80
      12 h123.00
      24 h131.60
      YbH20.0864 h100.20
      12 h118.90
      24 h131.15
    Tools

    Get Citation

    Copy Citation Text

    Weide WANG, Huanbei CHEN, Shishuai LI, Dongxu YAO, Kaihui ZUO, Yuping ZENG. Preparation of Silicon Nitride with High Thermal Conductivity and High Flexural Strength Using YbH2-MgO as Sintering Additive [J]. Journal of Inorganic Materials, 2021, 36(9): 959

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: RESEARCH ARTICLE

    Received: Dec. 8, 2020

    Accepted: --

    Published Online: Dec. 9, 2021

    The Author Email: YAO Dongxu (yaodongxu@mail.sic.ac.cn)

    DOI:10.15541/jim20200705

    Topics