Journal of Inorganic Materials, Volume. 35, Issue 12, 1398(2020)

An Injectable Composite Bone Cement Based on Mesoporous Borosilicate Bioactive Glass Spheres

Yuchen CHANG1... Ziyang LIN1, Xin XIE1, Zhangfan WU1, Aihua YAO1, Song YE1, Jian LIN1, Deping WANG1,* and Xu CUI2,* |Show fewer author(s)
Author Affiliations
  • 1School of Materials Science and Engineering, Tongji University, Shanghai 201804, China
  • 2Center for Human Tissues and Organs Degeneration, Institute of Biomedicine and Biotechnolgy, Shenzhen Institutes of Advanced Technology, Chinese Academy of Science, Shenzhen 518055, China
  • show less
    Figures & Tables(14)
    XRD patterns of the as-prepared MBGS
    TEM images of the as-prepared MBGS
    FT-IR spectra of the as-prepared MBGS
    (a) N2 adsorption-desorption isotherms and (b) pore size distributions of MBGS-20, MBGS-30, and MBGS-40
    SEM images of (a, d) BC-20, (b, e) BC-30, and (c, f) BC-40 bone cement specimens
    (a) Setting time and (b) compressive strength of BC-20, BC-30, and BC-40, respectively* indicates significant difference between groups, p<0.05
    (a) Force-displacement curves and (b) injectabilities of mesoporous borosilicate bone cements for different B2O3 contents* indicates significant difference between groups, p<0.05
    Photographs of the mesoporous borosilicate bone cement extruded from the syring
    Anti-washout properties of mesoporous borosilicate bone cements
    Morphologies of mesoporous borosilicate bone cement specimens after being shaken in PBS at 37 ℃ for 2, 5, 12, and 24 h, respectively
    XRD patterns of bone cement specimens after being immersed in SBF for 3, 7 and 14 d, respectively
    SEM images and EDS data of (a, d) BC-20, (b, e) BC-30, (c, f) BC-30 after being immersed in SBF for 14 d
    • Table 1.

      The compositions of MBGS/mol%

      View table
      View in Article

      Table 1.

      The compositions of MBGS/mol%

      GlassB2O3SiO2CaOP2O5
      MBGS-202040364
      MBGS-303030364
      MBGS-404020364
    • Table 2.

      Specific surface area, average pore diameter and total pore volume of the three groups of MBGS

      View table
      View in Article

      Table 2.

      Specific surface area, average pore diameter and total pore volume of the three groups of MBGS

      SampleSpecific surface area/(m2∙g-1)Average pore diameter/nmTotal pore volume/(mL∙g-1)
      MBGS-20161.7113.330.052
      MBGS-30176.9813.970.057
      MBGS-40214.2815.110.079
    Tools

    Get Citation

    Copy Citation Text

    Yuchen CHANG, Ziyang LIN, Xin XIE, Zhangfan WU, Aihua YAO, Song YE, Jian LIN, Deping WANG, Xu CUI. An Injectable Composite Bone Cement Based on Mesoporous Borosilicate Bioactive Glass Spheres[J]. Journal of Inorganic Materials, 2020, 35(12): 1398

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: RESEARCH LETTERS

    Received: Mar. 17, 2020

    Accepted: --

    Published Online: Mar. 10, 2021

    The Author Email: WANG Deping (wdpshk@tongji.edu.cn), CUI Xu (xu.cui@siat.ac.cn)

    DOI:10.15541/jim20200140

    Topics