Journal of Inorganic Materials, Volume. 35, Issue 1, 41(2020)

Hot-pressing Sintering of Double-A-layer MAX Phase Mo2Ga2C

Sen JIN1... Zuo-Tong WANG2, Ya-Qiong DU1, Qian-Ku HU1, Jian-Gong YU2 and Ai-Guo ZHOU1,* |Show fewer author(s)
Author Affiliations
  • 1School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000, China
  • 2School of Mechanical and Power Engineering, Henan Polytechnic University, Jiaozuo 454003, China
  • show less
    Figures & Tables(6)
    XRD patterns of samples sintered at different temperatures
    Photo of the sample sintered at 850 ℃ for 2 h, in which the glittering particles on samples surface marked by red cycles are precipitated Ga
    (a) XRD patterns of hot-pressed Mo2Ga2C samples with different sintering time, and (b) intensity ratios of (008) peak and (103) peak
    Low and high magnification SEM images of Mo2Ga2C powders
    (a-d) SEM images of samples sintered at 750 ℃ for 2, 4, 6 and 8 h, (e) high-magnification image of (d), and (f) SEM image of sample sintered at 850 ℃ for 2 h
    • Table 1. Effect of sintering time on sample density and relative density

      View table
      View in Article

      Table 1. Effect of sintering time on sample density and relative density

      Sintering time/hDensity/(g·cm-3)Relative density/%
      25.4468.8
      46.6984.6
      67.2892.0
      87.8198.8
    Tools

    Get Citation

    Copy Citation Text

    Sen JIN, Zuo-Tong WANG, Ya-Qiong DU, Qian-Ku HU, Jian-Gong YU, Ai-Guo ZHOU. Hot-pressing Sintering of Double-A-layer MAX Phase Mo2Ga2C[J]. Journal of Inorganic Materials, 2020, 35(1): 41

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: RESEARCH PAPER

    Received: Jun. 19, 2019

    Accepted: --

    Published Online: Feb. 24, 2021

    The Author Email: ZHOU Ai-Guo (zhouag@hpu.edu.cn)

    DOI:10.15541/jim20190296

    Topics