Spectroscopy and Spectral Analysis, Volume. 42, Issue 7, 2082(2022)

The Technological Characteristics of Housi’ao Sagger and Its Influence on Influence on the Color of Celadon Glaze

Jun-ming WU1,*... Yue-xia SANG1,1; *;, Nai-zhang ZHENG1,1;, Jian-ming ZHENG2,2;, Lin WU1,1; and Ri-qin SHAN1,1; |Show fewer author(s)
Author Affiliations
  • 11. Art and Archabology School, Jingdezhen Ceramic Institute, Jingdezhen 333001, China
  • 22. School of Materials Science and Engineering, Fudan University, Shanghai 200433, China
  • show less
    Figures & Tables(18)
    Photo images of typical sagger and celadon samples excavated from Housi’ao kiln site
    Box diagram of porcelain sagger and common sagger (a) SiO2, (b) Al2O3 contents in Housi’ao kiln site of Tang and Five Dynasties
    Content distribution diagram of porcelain sagger and common sagger SiO2, Al2O3 (a), TiO2 and Fe2O3 (b) in Housi’ao kiln site of Tang and Five Dynasties
    Content distribution diagram of Sagger and porcelain clay SiO2, Al2O3 (a), TiO2 and Fe2O3 (b) in Housi’ao kiln site of Tang and Five Dynasties
    Distribution diagram of SiO2, Al2O3 (a), TiO2 and Fe2O3 (b) contents of porcelain sagger and celadon bodies in Housi’ao kiln site in Tang and Five Dynasties
    Microstructure of porcelain sagger (a) and common sagger (b) in Housi’ao Kilnsite of Tang and Five Dynasties (orthogonal light)
    Depth-of-field microscope photographs (a) and (b) frequency distribution of coarse particles of common sagger of Housi’ao kiln site of Tang and Five Dynastie
    Photo images of porcelain sagger sagger internal and external(a): Internal; (b): External
    Celadon samples setting mode in the common sagger (a) and porcelain sagger (b)
    The CIE spatial chromaticity of celadon glazes
    Microstructure of Mi’se celadon (a) and common celadon (b) glazes in Housi’ao Kiln site of Tang and Five Dynasties (orthogonal light)
    • Table 1. Chemical composition of Porcelain sagger of Tang and Five Dynasties excavated

      View table
      View in Article

      Table 1. Chemical composition of Porcelain sagger of Tang and Five Dynasties excavated

      编号Na2OMgOAl2O3SiO2K2OCaOTiO2Fe2O3
      T-CX-10.850.4316.2374.993.300.401.041.96
      T-CX-21.040.6615.0675.963.220.360.682.02
      T-CX-30.730.5316.1474.673.060.391.491.99
      W-CX-11.190.4416.5474.782.830.420.772.03
      W-CX-21.140.4716.3574.522.920.360.952.02
      W-CX-31.010.3816.6374.622.680.610.712.35
    • Table 2. Chemical composition of common sagger matrix and coarse aggregate of Tang and Five Dynasties excavated from Housi ’ao kiln site (Wt%)

      View table
      View in Article

      Table 2. Chemical composition of common sagger matrix and coarse aggregate of Tang and Five Dynasties excavated from Housi ’ao kiln site (Wt%)

      编号Na2OMgOAl2O3SiO2K2OCaOTiO2Fe2O3
      T-PX-1-J0.220.4716.4675.212.450.510.972.70
      T-PX-2-J1.150.4410.7181.492.230.261.211.51
      T-PX-3-J0.810.4519.8771.113.030.450.832.45
      T-PX-1-C0.920.158.3686.042.760.240.110.42
      T-PX-2-C0.340.255.9191.240.390.190.040.64
      T-PX-3-C1.050.1911.2881.034.510.150.110.67
      W-PX-1-J1.010.4316.3474.123.650.330.822.31
      W-PX-2-J0.770.3616.9874.213.570.380.861.87
      W-PX-3-J1.530.3116.9875.691.250.280.702.26
      W-PX-1-C0.860.019.2284.753.230.150.250.55
      W-PX-2-C0.340.284.0493.230.410.120.050.52
      W-PX-3-C0.220.062.7095.280.260.110.050.44
    • Table 3. Chemical composition of porcelain stone and porcelain clay near Housi’ao kiln site (Wt%)

      View table
      View in Article

      Table 3. Chemical composition of porcelain stone and porcelain clay near Housi’ao kiln site (Wt%)

      编号Na2OMgOAl2O3SiO2K2OCaOTiO2Fe2O3烧失量
      后司岙瓷石1.291.3313.9877.512.480.920.111.38-
      白洋湖瓷土1.130.4215.1276.322.570.490.912.056.83
      后司岙瓷土1.010.3816.6774.622.680.610.712.358.59
      后司岙瓷土滤渣0.850.4611.1581.732.380.530.381.52-
    • Table 4. Chemical composition of tang and Five Dynasties celadon bodies unearthed at Housi’ao Kiln site (Wt%)

      View table
      View in Article

      Table 4. Chemical composition of tang and Five Dynasties celadon bodies unearthed at Housi’ao Kiln site (Wt%)

      编号Na2OMgOAl2O3SiO2K2OCaOTiO2Fe2O3
      T-MS-1-b0.690.4916.1075.383.010.590.821.95
      T-MS-2-b1.280.5716.5174.493.130.770.801.45
      T-MS-3-b1.070.5714.5377.122.680.510.741.78
      T-PT-1-b1.070.6916.6874.302.850.410.802.20
      T-PT-2-b1.010.4617.1173.882.950.401.012.18
      T-PT-3-b1.470.5716.5874.113.010.410.921.94
      W-MS-1-b0.640.4916.9874.812.980.360.851.89
      W-MS-2-b0.710.4316.7675.292.860.440.701.83
      W-MS-3-b1.320.4917.5873.373.170.670.761.63
      W-PT-1-b1.060.4617.5473.582.810.670.882.00
      W-PT-2-b1.470.3714.7874.943.332.741.111.25
      W-PT-3-b1.000.5118.3273.472.650.350.821.88
    • Table 5. Chemical composition of tang and Five Dynasties celadon glazes unearthed at Housi’ao Kiln site (Wt%)

      View table
      View in Article

      Table 5. Chemical composition of tang and Five Dynasties celadon glazes unearthed at Housi’ao Kiln site (Wt%)

      编号Na2OMgOAl2O3SiO2K2OCaOTiO2Fe2O3MnO
      T-MS-1-g0.483.6411.2764.981.5414.960.331.790.35
      T-MS-2-g0.643.6913.0065.821.5612.420.321.550.26
      T-MS-3-g0.794.3712.1663.621.7014.040.361.960.37
      T-PT-1-g0.642.9512.3564.501.7212.560.341.540.64
      T-PT-2-g0.384.0311.4265.171.5714.630.291.500.34
      T-PT-3-g1.622.5311.0466.811.8513.570.301.280.26
      W-MS-1-g0.264.3111.2864.571.4915.450.271.340.21
      W-MS-2-g0.813.4411.8162.241.9516.510.371.860.35
      W-MS-3-g0.783.3911.6567.111.9012.670.291.210.29
      W-PT-1-g0.982.9412.5665.081.2311.560.692.10.24
      W-PT-2-g0.033.8512.5464.611.9213.900.391.760.35
      W-PT-3-g0.033.1412.3164.221.6115.900.351.440.18
    • Table 6. Chromaticity of common celadon and Mi’se celadon glazes unearthed at Housi’ao Kiln site

      View table
      View in Article

      Table 6. Chromaticity of common celadon and Mi’se celadon glazes unearthed at Housi’ao Kiln site

      编号XYZxyzL*a*b*
      T-MS-125.9828.3623.990.330.360.1960.21-4.0410.62
      T-MS-227.4830.0825.590.330.360.2161.73-4.4310.59
      T-MS-325.5927.6622.510.340.370.2059.58-2.9112.06
      T-PT-120.7121.3815.450.360.370.2153.361.9015.26
      T-PT-222.3923.0015.580.370.380.2254.722.4017.70
      T-PT-319.4120.9116.450.340.370.2152.85-2.3512.20
      W-MS-127.8730.3126.620.330.360.2461.92-3.699.29
      W-MS-228.1129.9925.680.340.360.2261.65-1.5810.31
      W-MS-328.3030.8625.090.340.370.2362.39-4.0112.53
      W-PT-120.8621.3614.270.370.380.2153.342.6917.98
      W-PT-222.9624.0117.330.360.370.1856.090.6415.93
      W-PT-319.0020.0315.880.350.360.2151.87-0.2011.76
    • Table 7. Average physical and chemical properties of porcelain sagge and common sagger

      View table
      View in Article

      Table 7. Average physical and chemical properties of porcelain sagge and common sagger

      编号数量气孔率
      /%
      体积密度
      /(g·cm-3)
      吸水率
      /%
      T-CX61.092.200.50
      W-CX62.122.240.95
      T-PX68.741.954.51
      W-PX67.622.044.04
    Tools

    Get Citation

    Copy Citation Text

    Jun-ming WU, Yue-xia SANG, Nai-zhang ZHENG, Jian-ming ZHENG, Lin WU, Ri-qin SHAN. The Technological Characteristics of Housi’ao Sagger and Its Influence on Influence on the Color of Celadon Glaze[J]. Spectroscopy and Spectral Analysis, 2022, 42(7): 2082

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: Orginal Article