Acta Physica Sinica, Volume. 69, Issue 17, 174208-1(2020)
Figures & Tables(5)
Fig. 1. PL emission spectra of KDP crystal with different flux irradiations measured from (a) 200 to 400 nm and (b) 400 to 800 nm.
Fig. 2. PL emission spectra of KDP crystals with different flux irradiations measured from 400 to 800 nm: (a) Retired; (b) 9.0 J/cm2; (c) 11.5 J/cm2. The black solid lines represent the experiment spectra, the red dotted lines represent the simulated spectra, and the blue lines represent the Gaussian fitting curve.
Fig. 3. PL emission spectra of KDP crystals with different flux irradiations were measured from 200 to 400 nm: (a) Retired; (b) 9.0 J/m2; (c) 11.5 J/m2. The black solid lines represent the experiment spectra, the red dotted lines represent the simulated spectra and blue lines represent the Gaussian fitting curve.
Table 1. Parameters of peaks with Gaussian fitting for samples irradiated by different flux irradiations measured from 400 to 800 nm.
View tableView in ArticleTable 1. Parameters of peaks with Gaussian fitting for samples irradiated by different flux irradiations measured from 400 to 800 nm.
Peak Position/nm Area/arb. units. FWHM/nm Retired 9.0 J/cm2 11.5 J/cm2 Retired 9.0 J/cm2 11.5 J/cm2 Retired 9.0 J/cm2 11.5 J/cm2 A 420.27 430.52 423.87 0.12 0.35 0.13 15.38 45.14 19.41 B 479.19 480.94 480.54 2.23 1.50 1.12 88.95 91.53 80.68 C 587.24 578.64 593.58 2.40 1.68 2.51 116.60 140.89 122.17
Table 2. Parameters of peaks with Gaussian fitting for samples irradiated by different flux irradiations measured from 200 to 400 nm.
View tableView in ArticleTable 2. Parameters of peaks with Gaussian fitting for samples irradiated by different flux irradiations measured from 200 to 400 nm.
Peak Position/nm Area/arb. units FWHM/nm Retired 9.0 J/cm2 11.5 J/cm2 Retired 9.0 J/cm2 11.5 J/cm2 Retired 9.0 J/cm2 11.5 J/cm2 A 231.55 2.00 32.89 B 268.01 269.61 269.04 3.33 2.26 2.29 71.66 62.61 67.12 C 324.02 326.95 326.82 2.67 1.94 1.35 91.90 83.30 79.92
Tools
Get Citation
Copy Citation Text
Xiang-Cao Li, Bao-An Liu, Meng Li, Chun-Yan Yan, Jie Ren, Chang Liu, Xin Ju.
Paper Information
Category:
Received: Apr. 1, 2020
Accepted: --
Published Online: Jan. 4, 2021
The Author Email:
© Copyright 2018-2021 | Chinese Laser Press.
All Rights Reserved 沪ICP备15018463号-20