Multi-scale Failure Behavior of Cathode in Lithium-ion Batteries Based on Stress Field

Ying CHEN1... Weiling LUAN1,*, Haofeng CHEN1,2,* and Xuanchen ZHU2 |Show fewer author(s)
Author Affiliations
  • 11. Key Laboratory of Power Battery Systems and Safety (CPCIF), Key Laboratory of Pressure Systems and Safety (MOE), School of Mechanical and Power Engineering, East China University of Science and Technology, Shanghai 200237, China
  • 22. Department of Mechanical & Aerospace Engineering, University of Strathclyde, Glasgow G11XJ, UK
  • show less
    Figures & Tables(8)
    Multi-scale damage of NCM523 after electrochemical cycles
    Schematic illustration of active particle during the lithiation/ delithiation process
    Crack initiation and propagation of active particle of diameter of 3 μm under the current density of 0.37 A/m2[17]
    Integrated fracture criteria diagram for NCM particles[17]
    SEM images of NCM cathode after cyclic charging- discharging test
    (a) Schematic illustration of electrode during the lithiation/ delithiation process, whereby NCM active layer being coated on the Al current collector, and (b) boundary condition and the load applied to electrode during the lithiation stage[20]
    Shakedown and ratcheting limit curves of NCM material with varying thickness of 10, 20 and 30 µm[20]
    (a) Contour map of plastic strain range and ratcheting strain of NCM active layer of 20 µm thickness for load point (1,1) and (b) picture of NCM cathode before (left) and after (right) cyclic charging-discharging test[20]
    Tools

    Get Citation

    Copy Citation Text

    Ying CHEN, Weiling LUAN, Haofeng CHEN, Xuanchen ZHU. Multi-scale Failure Behavior of Cathode in Lithium-ion Batteries Based on Stress Field[J]. Journal of Inorganic Materials, 2022, 37(8): 918

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: RESEARCH ARTICLE

    Received: Dec. 20, 2021

    Accepted: --

    Published Online: Jan. 10, 2023

    The Author Email: LUAN Weiling (luan@ecust.edu.cn), CHEN Haofeng (haofeng.chen@ecust.edu.cn)

    DOI:10.15541/jim20210777

    Topics