<trans-title xml:lang="en">Mechanical Properties and Thermal Conductivity of Si<sub>3</sub>N<sub>4</sub> Ceramics with Composite Sintering Additives </trans-title>

Shi FU; Zengchao YANG; Honghua LI; Liang WANG; Jiangtao LI

doi:10.15541/jim20220101

Journal of Inorganic Materials, Volume. 37, Issue 9, 947(2022)

Mechanical Properties and Thermal Conductivity of Si₃N₄ Ceramics with Composite Sintering Additives

Shi FU1...2, Zengchao YANG1, Honghua LI1,*, Liang WANG1, and Jiangtao LI12,* |Show fewer author(s)

¹1. Key Laboratory of Cryogenics, Technical Institute of Physics and Chemistry, Chinese Academy of Science, Beijing 100190, China

²2. Center of Materials Science and Optoelectronics Engineering, University of the Chinese Academy of Science, Beijing 100049, China

show less

Abstract Get PDF(in Chinese)

Figures & Tables(7)

1. XRD patterns of Si₃N₄ceramics with different additive systems prepared by hot pressing sintering

Download full size

View in Article

2. SEM images of the polished surfaces of Si₃N₄ ceramics with different additive systems prepared by hot pressing sintering

Download full size

View in Article

3. XRD patterns of Si₃N₄ceramics with different additive systems after annealing

Download full size

View in Article

4. SEM images of the polished surfaces of Si₃N₄ceramics with different additive systems after annealing

Download full size

View in Article

$(a) Average grain size, (b) bending strength, (c) fracture toughness, and (d) thermal conductivity changing with radius of rare earth ion of Si3N4 ceramics before and after annealing$

5. (a) Average grain size, (b) bending strength, (c) fracture toughness, and (d) thermal conductivity changing with radius of rare earth ion of Si₃N₄ ceramics before and after annealing

Download full size

View in Article

6. Microstructures of Si₃N₄ceramic samples before and after annealing

Download full size

View in Article

Table 1. Properties of Si₃N₄ceramic samples prepared by hot pressing sintering

View table

View in Article

Table 1. Properties of Si₃N₄ceramic samples prepared by hot pressing sintering

Sample	Ionic radius/nm	Relative density/%	Grain size/μm	Vickers’ hardness/GPa	Flexural strength/MPa	Fracture toughness/ (MPa·m^1/2)	Thermal conductivity/ (W·m^-1·K^-1)
ScM	0.073	99.36	0.72±0.32	14.58±0.25	905±36	8.21±0.09	54.7
LuM	0.085	99.53	0.9±0.40	14.75±0.20	785±25	8.01±0.12	49.6
YbM	0.086	99.49	0.97±0.47	14.75±0.27	759±20	8.03±0.16	49.7
YM	0.089	99.73	1.03±0.46	14.64±0.29	819±10	8.65±0.11	51.1
GdM	0.094	99.89	1.01±0.48	14.57±0.22	792±34	7.62±0.47	54.6
NdM	0.100	99.37	0.95±0.42	14.79±0.27	1115±49	7.19±0.10	53.9
LaM	0.106	99.21	0.9±0.41	15.37±0.33	978±39	7.25±0.10	52.8

Tools

Get Citation

Copy Citation Text

Shi FU, Zengchao YANG, Honghua LI, Liang WANG, Jiangtao LI. Mechanical Properties and Thermal Conductivity of Si₃N₄ Ceramics with Composite Sintering Additives [J]. Journal of Inorganic Materials, 2022, 37(9): 947

Download Citation

EndNote(RIS)BibTex Plain Text

Set citation alerts for article

Save article for my favorites