Journal of Inorganic Materials, Volume. 38, Issue 2, 177(2023)

Tensile Creep Behavior of Cansas-II SiCf/SiC Composites at High Temperatures

Kaikai JING*... Haoyang GUAN, Siyu ZHU, Chao ZHANG, Yongsheng LIU, Bo WANG, Jing WANG, Mei LI and Chengyu ZHANG |Show fewer author(s)
Figures & Tables(12)
Dimensions and shape of tensile and tensile creep specimen (unit: mm)
Tensile creep curves of 2D-SiCf/SiC at high temperatures
Tensile stress-strain curves of as-received and crept 2D-SiCf/SiC
Macroscopic morphologies of fractures of 2D-SiCf/SiC under different conditions
Morphologies of fracture oxidation zone of 2D-SiCf/SiC under different creep rupture conditions
Interface and fiber damage in 2D-SiCf/SiC during creeping at 1300 ℃/100 MPa
Longitudinal fiber microstructures of 2D-SiCf/SiC after crept
Larson-Miller plots for 2D-SiCf/SiC
  • Table 1. Basic properties of domestic second-generation Cansas-II silicon carbide fibers

    View table
    View in Article

    Table 1. Basic properties of domestic second-generation Cansas-II silicon carbide fibers

    Diameter/μm Density/(g·cm-3) Tensile strength/GPa Tensile modulus/GPa
    142.742.7270
  • Table 2. Tensile properties of 2D-SiCf/SiC composites

    View table
    View in Article

    Table 2. Tensile properties of 2D-SiCf/SiC composites

    Temperature/℃E/GPa σPLS/MPa σUTS/MPa ε/%
    RT2731152820.57
    12002591102490.74
    1300223922290.60
  • Table 3. Tensile creep properties of 2D-SiCf/SiC composites in air at high temperatures

    View table
    View in Article

    Table 3. Tensile creep properties of 2D-SiCf/SiC composites in air at high temperatures

    SpecimenTempera-ture/℃ Stress/MPa Steady-state creep strain rate/s-1Creep rupture time/h Creepstrain/%
    2D-SiCf/SiC12001001.86×10-10>5600.20
    12001104.95×10-10>5600.23
    12001202.16×10-9420.18
    12001408.45×10-70.10.21
    1300905.62×10-10>5000.28
    13001001.73×10-9700.20
    13001201.86×10-860.28
    1400801.32×10-9880.33
    14001001.46×10-81.60.57
    CVI-SiCf/SiC[13]1300752.3×10-9111.1
    1300906.2×10-833.4
    13001203.6×10-70.83
    13001503.0×10-60.14
    MI-SiCf/SiC[15]12041253.0×10-11>10000.25
    12041402.3×10-10>10000.31
    120415082.10.29
  • Table 4. Residual tensile properties of 2D-SiCf/SiC after creeping

    View table
    View in Article

    Table 4. Residual tensile properties of 2D-SiCf/SiC after creeping

    σUTS/MPa E/GPa σPLS/MPa ε/%
    As-received2822731150.57
    Crept1200 ℃/100 MPa211
    1200 ℃/110 MPa173209890.25
    1300 ℃/90 MPa138157550.17
Tools

Get Citation

Copy Citation Text

Kaikai JING, Haoyang GUAN, Siyu ZHU, Chao ZHANG, Yongsheng LIU, Bo WANG, Jing WANG, Mei LI, Chengyu ZHANG. Tensile Creep Behavior of Cansas-II SiCf/SiC Composites at High Temperatures[J]. Journal of Inorganic Materials, 2023, 38(2): 177

Download Citation

EndNote(RIS)BibTexPlain Text
Save article for my favorites
Paper Information

Category: EDITORIAL

Received: Jul. 29, 2022

Accepted: --

Published Online: Sep. 27, 2023

The Author Email: JING Kaikai (2247436229@qq.com)

DOI:10.15541/jim20220441

Topics