Journal of Inorganic Materials, Volume. 36, Issue 2, 203(2021)
Figures & Tables(19)
. Schematic illustration for the synthesis steps of hollow Co/C composite and its effect for the resulting electrode
. (a) XRD pattern, (b) Raman spectrum, (c) XPS spectrum and (d) N2 adsorption/desorption isotherm of Co/C-700 with insert in (d) showing pore size distribution
. (a) TGA curve of Co/C-700 in air and (b) XRD pattern of the final product
. (a, b) TEM, (c) high-resolution TEM (HRTEM) images and (d) EDS elemental mappings (Co, C and O) of Co/C-700
. N2 adsorption/desorption isotherms (a) and pore size distributions (b) of UWC-700 and HEC-700
. High resolution XPS spectra of Co/C-700(a) C1s; (b) O1s; (c) Co2p
. Photograph of static adsorption test of HEC-700 and Co/C-700 after standing for 1 h
. Multi-cycle CV curves of Co/C-700 based symmetric cells at 1 mV∙s-1 (a) and increased rates (b), and multi-cycle CV curves of HEC-700 at 1 mV∙s-1 (c) and increased rates (d)
. CV curves of (a) Co/C-700 and (b) HEC-700 based symmetric cells with and without 0.2 mol∙L-1 Li2S6 at 1 mV∙s-1; (c) CV curves and (d) EIS plots of S@Co/C-700 and S@HEC-700 electrodes
. (a) Rate capabilities at various rates from 0.5C to 10C and (b) cycling stabilities at 1C for S@Co/C-700 and S@HEC-700 electrodes
. Voltage profiles of S@HEC-700 (a) and S@Co/C-700 (b) electrodes at various rates from 0.5C to 10C
. (a) Cycling stabilities of S@Co/C-700 and S@HEC-700 electrodes at 2C ; (b) Cycling performance of S@Co/C-700 at 5C and 10C
Table 1.
BET surface area and pore volume distribution of UWC-700, Co/C-700 and HEC-700
View tableView in ArticleTable 1.
BET surface area and pore volume distribution of UWC-700, Co/C-700 and HEC-700
Sample SBET/(m2∙g-1) Vtotal/(cm3∙g-1) Pore volume/% Micro Meso Macro UWC-700 15.09 0.026 1.76 98.24 0 Co/C-700 376.13 0.52 28.85 62.76 8.49 HEC-700 369.53 0.54 25.47 68.17 6.36
Tools
Get Citation
Copy Citation Text
Gaoyao JIN, Haichuan HE, Jie WU, Mengyuan ZHANG, Yajuan LI, Younian LIU.
Paper Information
Category: RESEARCH LETTERS
Received: Mar. 27, 2020
Accepted: --
Published Online: Nov. 24, 2021
The Author Email: LI Yajuan (yajuanli@csu.edu.cn)
© Copyright 2018-2021 | Chinese Laser Press.
All Rights Reserved 沪ICP备15018463号-20