Journal of Inorganic Materials, Volume. 34, Issue 1, 72(2019)

BN/CsPbX3 Composite Nanocrystals: Synthesis and Applications in White LED

Yu-Hui DONG... Shu-Yu ZENG, Bo-Ning HAN, Jie XUE, Ji-Zhong SONG, Hai-Bo ZENG, [in Chinese], [in Chinese], [in Chinese], [in Chinese], [in Chinese] and [in Chinese] |Show fewer author(s)
Author Affiliations
  • MIIT Key Laboratory of Advanced Display Materials and Devices, Institute of Optoelectronics & Nanomaterials, School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China
  • show less
    Figures & Tables(15)
    Scheme of the all-solid-state ball milling procedure for synthesis of CsPbX3 NCs (a) and optical image of large-scale red emission powder under UV light excitation (365 nm) (b)
    PL intensity of CsPbBr3 NCs powder with different size of grind medium under the same test condition
    PL intensity of CsPbBr3 NCs powder with different ball-to-powder ratio under the same condition
    (a) PL emission spectra of CsPbX3 NCs powder, the corresponding optical images under normal daylight and UV light (black background) were exhibited inside; (b) Color gamut spectra of perovskite NCs (the inner black line indicating NTSC)
    EDS information of CsPbI3 NCs powder(a) SEM image with corresponding atomic percentage information; (b) EDS spectrum of CsPbI3 NCs
    SEM images of CsPbX3 NCs
    PL spectra of CsPbBr3 NCs powder with various rotation speed of the planetary mill
    The air stability of CsPbI3 NCs powder (a) The PL stability exposed in air; (b) X-ray diffraction (XRD) pattern of CsPbI3 NCs powder; (c) Photographs of the powder samples with time changing under the sunlight (left) and UV light (right)
    The X-Ray diffraction spectra of CsPbX3 NCs powder with various halogen ratios
    The PL spectrum of CsPbI3 powder adding amount of 0.2 g of BN
    Analysis of air stability of CsPbI3 NCs (a) Stability test of CsPbI3 NCs powder with different BN quantity; (b) SEM image of CsPbI3 NCs; (c) Energy dispersive spectroscopy (EDS) mapping images of (b)
    Proof-of-concept demonstration of white LED by blending green and red Pe-NCs on a commercial blue LED chip (a) Schematically depicts the packing method of white LED; (b) EL spectra of three typical devices exhibiting (1) green-white, (2) white, and (3) red-white; (c) Photographs of the white LED under different operating voltage
    The stability of white-light LED (a) The luminance stability of white-light LED placed in the air measured at the voltage of 2.7 V; (b) The working stability of the white-light LED after continuous operating for 2 h
    • Table 1. Comprehensive comparisons for the representative perovskite NCs

      View table
      View in Article

      Table 1. Comprehensive comparisons for the representative perovskite NCs

      CsPbX3Emission peak/nmFWHM/nmCsPbX3Emission peak/nmFWHM/nm
      CsPbCl341723CsPbIBr255141
      CsPbCl2.14Br0.8643023CsPbI2Br60547
      CsPbCl2Br44727CsPbI2.14Br0.8664246
      CsPbClBr248338CsPbI368040
      CsPbBr353233
    • Table 2. Comparison of FWHM of CsPbX3 with typical solution synthesis

      View table
      View in Article

      Table 2. Comparison of FWHM of CsPbX3 with typical solution synthesis

      SampleSynthetic methodsFWHM/nmColor/nmRef.
      CsPbX3(X=Cl, Br, I)All-solid-state ball milling23-47417-680This work
      CsPbX3(X=Cl, Br, I)Supersaturated recrystallization12-39400-650[1]
      CsPbX3(CsPb(Br/Cl)3 -CsPbI3)Droplet-based microfluidic platform20-45470-690[2]
      CsPbX3(X=Cl, Br, I)Fast Anion-Exchange12-40410-700[3]
    Tools

    Get Citation

    Copy Citation Text

    Yu-Hui DONG, Shu-Yu ZENG, Bo-Ning HAN, Jie XUE, Ji-Zhong SONG, Hai-Bo ZENG, [in Chinese], [in Chinese], [in Chinese], [in Chinese], [in Chinese], [in Chinese]. BN/CsPbX3 Composite Nanocrystals: Synthesis and Applications in White LED[J]. Journal of Inorganic Materials, 2019, 34(1): 72

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: Research Articles

    Received: May. 2, 2018

    Accepted: --

    Published Online: Feb. 4, 2021

    The Author Email:

    DOI:10.15541/jim20180207

    Topics