Spectroscopy and Spectral Analysis, Volume. 42, Issue 8, 2499(2022)

Study on the Spectral Characteristics of Filled Amazonite

Yan-han WU*... Quan-li CHEN*;, Jun-qi LI, An-di ZHAO, Xuan LI and Pei-jin BAO |Show fewer author(s)
Author Affiliations
  • Gemmological Institute, China University of Geosciences(Wuhan), Wuhan 430074, China
  • show less
    Figures & Tables(9)
    Appearance of amazonite samples
    Zoom in partial filled amazonite to see bubbles
    The infrared reflection spectra of amazonite samples
    The Raman spectra of amazonite samples between 100 and 3 700 cm-1
    The Raman spectra of amazonite samples between 100 and 1500 cm-1
    (a)Raman spectra of translucent area and green area of AN2; (b)Raman spectra of undertint crystal of AN1
    Three-dimensional fluorescence spectra of amazonite samples
    • Table 1. Coventional gemmological characteristics of amazonite samples

      View table
      View in Article

      Table 1. Coventional gemmological characteristics of amazonite samples

      样品编号处理情况光泽透明度折射率(点测)相对密度紫外荧光LW紫外荧光SW
      AN1天然未充填玻璃光泽不透明1.522.555中-蓝白色惰性
      AN2天然未充填玻璃光泽不透明1.532.555中-蓝白色弱-蓝白色
      AN3天然未充填玻璃光泽微透明1.532.509弱-白色惰性
      AN4天然未充填玻璃光泽微透明1.532.519弱-白色惰性
      AT1充填处理蜡状光泽微透明1.532.556惰性惰性
      AT2充填处理蜡状光泽微透明1.532.538中-白色惰性
      AT3充填处理弱玻璃光泽微透明1.522.566中-白色惰性
      AT4充填处理蜡状光泽微透明1.532.531中-白色惰性
    • Table 2. The analysis of three-dimensional fluorescence spectrum of amazonite samples

      View table
      View in Article

      Table 2. The analysis of three-dimensional fluorescence spectrum of amazonite samples

      样品编号Ex激发光源
      波长/nm
      Em发射光源
      波长/nm
      荧光中心
      相对强度
      AN12843043 221
      AN22823044 931
      AN32923128 069
      AN42763047 412
      AT12843044 772
      AT22923127 681
      AT32823042 551
      AT42843044 418
    Tools

    Get Citation

    Copy Citation Text

    Yan-han WU, Quan-li CHEN, Jun-qi LI, An-di ZHAO, Xuan LI, Pei-jin BAO. Study on the Spectral Characteristics of Filled Amazonite[J]. Spectroscopy and Spectral Analysis, 2022, 42(8): 2499

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: Orginal Article

    Received: Jul. 7, 2021

    Accepted: --

    Published Online: Mar. 17, 2025

    The Author Email: WU Yan-han (1609212960@qq.com)

    DOI:10.3964/j.issn.1000-0593(2022)08-2499-07

    Topics