Photonics Research, Volume. 9, Issue 8, 1559(2021)
Water-stable CsPbBr3 perovskite quantum-dot luminous fibers fabricated by centrifugal spinning for dual white light illumination and communication
Figures & Tables(12)
Fig. 2. (a) Centrifugal spinning process. PQD-PS fibers under (b) visible light and (c) UV light.
Fig. 3. (a) Mechanical treatment before PL measurement. (b) Centrifugal spinning fibers and fiber pieces under visible light and UV light. (c) PL measurement setup.
Fig. 4. Experimental setup of the visible light communication system.
Fig. 5. Structural analyses of
Fig. 6. (a) SEM image of PQD fibers. (b) XRD patterns of PS and PQD-PS fibers. (c) Time-resolved fluorescence measurement of the PQD-PS fibers (inset: single PQD fiber under ambient light and UV light). (d) Absorption and emission spectra of PQD-PS fibers.
Fig. 7. Emission spectra of PQD-PS fibers after (a) exposure to air and (b) immersion in water for one week. (c) Emission spectra of PQD-PS fibers after immersion in water for 11 months (inset: fibers soaking in water for 11 months under UV light). (d) PL intensity of fibers after stability test. (e) PL peak wavelength trend of PQD-PS fibers during water immersion. (f) PL decay curves of PQD-PS fibers after immersion in water and exposure to air.
Fig. 8. XRD patterns of PQD-PS fibers after (a) immersion in water, (b) exposure to air, and (c) exposure to UV light.
Fig. 9. PQD-PS fibers soaking in hexane under (a) visible light and (b) UV light. PQD-PS fibers after soaking in hexane and ultrasonic treatment under (c) visible light and (d) UV light. Hexane (right) and hexane after ultrasonic treatment (left) under (e) visible light and (f) UV light.
Fig. 10. (a) EL spectrum of QD-based white LEDs. (b) Color coordinates and color gamut of QD-based white LEDs plotted on the CIE1931 chromaticity diagram. (c) Frequency response of the LD, LD + YAG white light, LD + PQD-PS fibers, LD + CdSe/ZnS PDMS film, and LD + PQD-PS + CdSe/ZnS white light. (d) The
Table 1. PLQY Stability of PQD-PS Fibers
View tableView in ArticleTable 1. PLQY Stability of PQD-PS Fibers
Stability Test 7 Days 2 Weeks 5 Months Exposure to air 45.1% 43.5% 15.6% Immersion in water 54.9% 44.4% 44.4%
Table 2. PLQY Stability of CsPbBr3 with Different Composites
View tableView in ArticleTable 2. PLQY Stability of CsPbBr3 with Different Composites
at Composites Original PLQY Relative PLQY Refs. POSS 62% 98% (water, 2.5 months) [ 50 ]TDPA 68% [ 51 ]PMMA 45% 75% (humidity, 3 days) [ 52 ]EC 37.2% 87% (air, 6 days) [ 53 ]SBS 23% [ 54 ]PS 48% 70% (water, 8 days) [ 27 ]EVA 40.5% [ 55 ]PS 44% 82% (water, 24 h) [ 56 ]PS 23.3% 83% (water, 3 months) [ 57 ]S-AIM 75.6% 51% (water, 3.5 months) [ 21 ]SR/PVP 24% 85% (moist air, 5 days) [ 58 ]This work 53.7% 81% (air, 2 weeks) 83% (water, 5 months)
Tools
Get Citation
Copy Citation Text
Binhai Yu, Shunming Liang, Fengyi Zhang, Zongtao Li, Bin Liu, Xinrui Ding. Water-stable CsPbBr3 perovskite quantum-dot luminous fibers fabricated by centrifugal spinning for dual white light illumination and communication[J]. Photonics Research, 2021, 9(8): 1559
Paper Information
Category: Optical and Photonic Materials
Received: Apr. 7, 2021
Accepted: Jun. 20, 2021
Published Online: Jul. 28, 2021
The Author Email: Xinrui Ding (dingxr@scut.edu.cn)
© Copyright 2018-2021 | Chinese Laser Press.
All Rights Reserved 沪ICP备15018463号-20