Journal of Radiation Research and Radiation Processing, Volume. 42, Issue 5, 050801(2024)

Neutron irradiation related interfacial defects in lead zirconate titanate thick film

Maoyang PENG1...2, Dechao MENG1,* and Zhengping FU2 |Show fewer author(s)
Author Affiliations
  • 1Microsystem and Terahertz Research Center, Institute of Electronic Engineering,China Academy of Engineering Physics, Mianyang 621999, China
  • 2College of Nanoscience and Technology, University of Science and Technology of China, Suzhou 215123, China
  • show less
    Figures & Tables(8)
    Diagram of the decay rate of the dielectric constant of PZT thin films, ceramics and thick films under neutron irradiation[5](color online)
    [in Chinese]
    P-E loops of PZT with pre-irradiation and neutron irradiation fluxes of 1011 cm-2, 1012 cm-2 and 1013 cm-2 (color online)
    (a) Dielectric constant of PZT with pre-irradiation and neutron injection of 1011 cm-2, 1012 cm-2, and 1013 cm-2; (b) dielectric loss of PZT with pre-irradiation and neutron irradiation injection of 1011 cm-2, 1012 cm-2, and 1013 cm-2
    Leakage current characteristics of PZTs with pre-irradiation and neutron irradiation fluxes of 1011 cm-2, 1012 cm-2, and 1013 cm-2
    Simulation diagram of PZT interface changes before and after neutron irradiation
    • Table 1. Changes in defect activation energy (Ed), defect concentration (Nt), and defect capture area (Sigma) in PZT before and after neutron irradiation with 1011 cm-2, 1012 cm-2, and 1013 cm-2

      View table
      View in Article

      Table 1. Changes in defect activation energy (Ed), defect concentration (Nt), and defect capture area (Sigma) in PZT before and after neutron irradiation with 1011 cm-2, 1012 cm-2, and 1013 cm-2

      中子注量 / cm-2

      Neutron irradiation fluxes

      缺陷激活能 / eV

      Ed 

      缺陷浓度 / cm-3

      Nt

      缺陷俘获面积 / cm2

      Sigma

      00.96.9×10168.5×10-20
      10111.65.6×10166.5×10-20
      10121.73.3×10165.3×10-20
      10132.010151.1×10-19
    • Table 2. Percent change in residual polarization intensity and coercive field of PZT with pre-irradiation and neutron irradiation fluxes of 1011 cm-2, 1012 cm-2, and 1013 cm-2

      View table
      View in Article

      Table 2. Percent change in residual polarization intensity and coercive field of PZT with pre-irradiation and neutron irradiation fluxes of 1011 cm-2, 1012 cm-2, and 1013 cm-2

      中子注量 / cm-2 Neutron irradiation fluxes2Pr / (μC∙cm-2)2Ec / ( kV∙cm-1)
      067.440.7
      101159.939.0
      101256.138.8
      101340.934.0
    Tools

    Get Citation

    Copy Citation Text

    Maoyang PENG, Dechao MENG, Zhengping FU. Neutron irradiation related interfacial defects in lead zirconate titanate thick film[J]. Journal of Radiation Research and Radiation Processing, 2024, 42(5): 050801

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: RADIATION PHYSICS

    Received: Mar. 26, 2024

    Accepted: Jul. 15, 2024

    Published Online: Jan. 2, 2025

    The Author Email: MENG Dechao (孟德超)

    DOI:10.11889/j.1000-3436.2024-0024

    Topics