Journal of Inorganic Materials, Volume. 39, Issue 5, 531(2024)
Figures & Tables(11)
1. Sintering trajectories of MAGS-0.1 ceramics with 0.1%, 0.2% and 0.5% MgF2 and the unaided MAGS-0.1 ceramics
2. Variations of the shrinkage and shrinkage rate of MAGS-0.1 ceramic green bodies containing 0 and 0.2% MgF2 as a function of temperature
3. TG-DSC curves of MAGS-0.1 powder containing 10% MgF2 and XRD patterns of MAGS-0.1 powder containing 10% MgF2 after heating and holding at different temperatures
5. Phase compositions of powder, pre-sintered and transparent ceramic samples
6. Surface SEM images and grain size distributions of MAGS-0.1 ceramics with different additive contents after pressureless presintering and chemical etching
7. Surface SEM images and grain size distributions of MAGS-0.1 ceramics after HIP sintering and chemical etching
8. Appearance images of MAGS-0.1 transparent ceramics without additive and with 0.2% MgF2
9. Optical polarized transmission micrographs of transparent ceramics without additive and with 0.2% MgF2
10. Optical properties of samples with different additive contents and sizes
11. Weibull plots of fracture strength for MAGS-0.1 transparent ceramics
Tools
Get Citation
Copy Citation Text
Zhaoyang LÜ, Yong XU, Jiuyan YANG, Guangsheng TU, Bingtian TU, Hao WANG.
Paper Information
Category:
Received: Dec. 21, 2023
Accepted: --
Published Online: Jul. 8, 2024
The Author Email: WANG Hao (shswangh@whut.edu.cn)
© Copyright 2018-2021 | Chinese Laser Press.
All Rights Reserved 沪ICP备15018463号-20