Failure probability calculations of silicon carbide composite claddings under loss-of-coolant accidents
Silicon carbide (SiC) composite claddings are candidate solutions for accident resistant fuel claddings in light water reactors.
This study aims to estimate the failure probability of a double-layer structured SiC cladding under a loss-of-coolant accident (LOCA).
Based on a failure probability calculation method for SiC composite cladding, a quasi-steady state method was used to simulate and calculate the SiC composite cladding failure probability under transient conditions. Sensitivity analysis of the two characteristic parameters of Weibull distribution was performed by analyzing the proportion of various stresses under accident conditions. The effects of different burn-up conditions on the failure probability were investigated, and the failure probability of the cladding under different layer thickness ratios was simulated.
Simulation results indicate that the transient failure probability of SiC composite claddings is significantly affected by changes in the proportion of the composite layer and Weibull parameter, as well as the occurrence of LOCAs under different burn-up conditions. This study makes contribution to the development and design of accident resistant fuel claddings, providing reference for further investigations on the failure probability of SiC composite claddings.
Get Citation
Copy Citation Text
Liwen CAO, Boquan YI, Zulong HAO. Failure probability calculations of silicon carbide composite claddings under loss-of-coolant accidents[J]. NUCLEAR TECHNIQUES, 2023, 46(9): 090603
Category: Research Articles
Received: Oct. 10, 2022
Accepted: --
Published Online: Oct. 8, 2023
The Author Email: