Preparation and Luminescent Properties of a Ca2SnO4∶Tb3+ Phosphor
A novel green emitting phosphor, Tb3+-doped Ca2SnO4, was prepared by the solid-state reaction. X-ray powder diffraction (XRD) analysis confirmed the formation of Ca2SnO4∶Tb3+. Photoluminescence measurements indicated that the phosphor exhibits bright green emission at about 543 nm under UV excitation. The excitation spectra of Ca2-xTbxSnO4 appear to have a red shift with main peak from 254 to 260 nm. The emission spectra of Ca2-xTbxSnO4 have four peaks ascribed to 5D4—7FJ (where J=6, 5, 4, 3) transitions of Tb3+ ions. Under the condition of low Tb3+ concentration, the 5D4—7F6 transition of Tb3+ showed a stark energy level split to three split peaks and the peak intensity of 481nm firstly increased with increasing Tb3+ concentration, then decreased. The dependence of luminescent intensity of Ca2SnO4∶Tb3+ phosphor on the Tb3+ concentration was studied, and the results show that the luminescence intensity firstly increased with increasing Tb3+ concentration, then decreased, and reached the maximal value at 9 mol% Tb3+. According to the Dexter theory, the authors confirmed the concentration quenching mechanism of Tb3+ in Ca2SnO4. The fluorescence lifetime of phosphor analysis shows that the average lifetime is 4.4 ms. The results indicated that Ca2SnO4∶Tb3+ could be a potential candidate as a green-emitting powder phosphor.
Get Citation
Copy Citation Text
QIU Gui-ming, XU Cheng-ke, HUANG Chong. Preparation and Luminescent Properties of a Ca2SnO4∶Tb3+ Phosphor[J]. Spectroscopy and Spectral Analysis, 2011, 31(11): 2906
Received: Oct. 3, 2010
Accepted: --
Published Online: Dec. 22, 2011
The Author Email: Gui-ming QIU (gmqiu@stu.edu.cn)