Journal of Inorganic Materials, Volume. 38, Issue 1, 105(2023)
TiAl alloy has excellent properties of low density and high specific strength, which is a potential structural material for aero-engine. The service temperature of TiAl alloy is limited in the range of 700-900 ℃, which is further improved by preparation of high temperature thermal protection coating. In the present work, a new type of TiAlCrY/YSZ coating was prepared on the TiAl alloy by plasma spray technologies, of which long-term service performance at high temperature was compared with the traditional NiCrAlY/YSZ coating. It was found that the TiAlCrY/YSZ coating remained intact after served 300 h at 1100 ℃ in the air, showing excellent high temperature performance, while the service lifetime of the NiCrAlY/YSZ coating at 1100 ℃ was less than 100 h. The microstructure observation found that a continuous and dense TGO composed of Al2O3 was continuously formed on the TiAlCrY bonding coating, suggesting that TiAlCrY coating has good interfacial compatibility with the YSZ top coating. Moreover, the thickness of TGO was still less than 8 μm after served 300 h at 1100 ℃ in the air. As compared with traditional NiCrAlY/YSZ coating, the TiAlCrY/YSZ coating is a more suitable high temperature thermal coating ever for TiAl alloys.
Get Citation
Copy Citation Text
Yangyang PAN, Bo LIANG, Du HONG, Zhixiang QI, Yaran NIU, Xuebin ZHENG.
Category: RESEARCH ARTICLE
Received: Jun. 11, 2022
Accepted: --
Published Online: Sep. 25, 2023
The Author Email: LIANG Bo (liangbo@ysu.edu.cn)