Effect of Heat Treatment on Properties of Li2O-Al2O3A-SiO2 System Glass
The physical properties of the Li 2O Al 2O 3 SiO 2 system based zero expansion glass ceramic of V02 have been measured during a linearly temperature raise. There is a significant change in a narrow temperature range for all physical properties caused by the phase transformation. The refractive index increases from 1.5258 to 1.5433. The density increases from 2.563 to 2.576 g/cm 3. The expansion coefficient decrease from 41.5×10 -7 /℃ to near zero. The Knoop hardness increases from 57.8 MPa to 76.4 MPa. The total linear shrinkage is 1.12%. The optical transmission at short wavelength region decreases first and then increases with heat treatment temperature raise. Some useful points were suggested for controlled crystallization of large glass mirror blank.
Get Citation
Copy Citation Text
[in Chinese], [in Chinese], [in Chinese], [in Chinese], [in Chinese]. Effect of Heat Treatment on Properties of Li2O-Al2O3A-SiO2 System Glass[J]. Acta Optica Sinica, 2002, 22(7): 886