Effect of Aluminum Sulfate Based Alkali-Free Liquid Accelerator Modified by Aluminum Formate on Cement Properties
Aluminum formate was used to modify aluminum sulfate based alkali-free liquid accelerator, and the performance index of alkali-free liquid accelerator modified by aluminum formate was tested in this paper. XRD, SEM, TG-DTG and hydration thermal analysis were used to analyze the effect of aluminum sulfate based alkali-free liquid accelerator modified by aluminum formate on the hydration process of cement. The results show that with the increase of aluminum formate content in aluminium sulfate based alkali-free liquid accelerator, the quick setting effect and strength of cement show a trend of increasing first and then decreasing. When the modified content of aluminum formate is 1% (based on the mass percentage of aluminum sulfate), the properties of cement with 8% modified aluminum sulfate based alkali-free liquid accelerator are as follows: initial setting time of 2 min 39 s, final setting time of 5 min 33 s, 1 d compressive strength of 13.2 MPa, 28 d compressive strength of 49.6 MPa, 28 d compressive strength ratio of 114%, and 90 d compressive strength retention rate of 123%, which meets the technical index requirements of the standard “Flash setting admixtures for shotcrete” (GB/T 35159—2017). When the modified content of aluminum formate exceeds 1%, a large amount of AFt inhibits the hydration reaction of C3S in cement, resulting in the early and late strength reduction.
Get Citation
Copy Citation Text
LIU Yuan, ZHU Fangfang, ZHANG Yuanyong, YANG Anxu, YANG Lin. Effect of Aluminum Sulfate Based Alkali-Free Liquid Accelerator Modified by Aluminum Formate on Cement Properties[J]. Bulletin of the Chinese Ceramic Society, 2024, 43(12): 4330
Category:
Received: Jun. 2, 2024
Accepted: Jan. 10, 2025
Published Online: Jan. 10, 2025
The Author Email: Lin YANG (ce.lyang@gzu.edu.cn)
CSTR:32186.14.