In this paper, the research results of 12.5 μm long-wavelength infrared InAs/GaSb superlattice focal plane arrays were reported. The superlattice structure was grown on GaSb substrate using molecular beam epitaxy (MBE) technology. The respective structure of absorption region is 15ML ( InAs) /7ML ( GaSb). The detector adopts PBπBN double barrier structure to suppress the dark current. A long-wave focal plane detector with the size of 1 024×1 024 and the pixel center-to-center distance of 18 μm was developed. The detector is packaged by a metal dewar, and a superlattice long-wavelength detector cryocooler assembly is formed by coupling with a refrigerator. At 60 K measurement, the detector has 50% cut-off wavelength of 12.5 μm. The detector has a peak detectivity of 6.6×10¹⁰ cm?Hz^1/2/W^{, dead pixels rate of 1.05% and a noise equivalent temperature difference (NETD) is 21.2 mK. The Infrared images of the test have been taken clearly using the infrared imaging detector.}