Journal of Applied Optics, Volume. 45, Issue 4, 841(2024)

Influence of PEG content on optical band gap and laser damage characteristics of porous films

Shaobin SUN1, Junqi XU1、*, Junhong SU1, Yang LI1, Tong WANG1, and Zheng LIU2
Author Affiliations
  • 1Shaanxi Province Thin Film Technology and Optical Test Open Key Laboratory, Xi'an Technological University, Xi'an 710021, China
  • 2Advanced Optical Manufacturing Technology Joint Laboratory, Xi'an Institute of Optics and Precision Mechanics of CAS, Xi'an 710119, China
  • show less

    TiO2 and SiO2 films with different porosity were prepared on quartz substrate and Si substrate respectively by sol-gel technique combined with spin coating method, and the optical and laser damage characteristics of both films were investigated. The optical band gap of the films was calculated based on the transmission spectral curves. It was found that the optical band gap increased with the increase of porosity, the optical band gap size of TiO2 films ranged from 3.75 eV to 3.97 eV, and that of SiO2 films ranged from 3.52 eV to 3.78 eV. The ellipsometry measurement results show that when the mass fraction of polyethylene glycol (PEG) was increased from 0, 0.8%, 4% to 8% at a wavelength of 1 064 nm, the porosity of TiO2 films increased from 11.5%, 14.1%, 30.9% to 38.7%, and the refractive index decreased from 2.063 5, 2.016 5, 1.748 1 to 1.640 9; the porosity of SiO2 films increased from 4.04%, 4.6%, 5.7% to 13.9%, and the refractive index decreased from 1.438 6, 1.435 8, 1.420 4 to 1.387 9. The extinction coefficients of all TiO2 and SiO2 film samples are better than 10?3 except for the TiO2 film with PEG mass fraction of 0.8%, which indicates that the absorption of the films is smaller. The laser induced damage threshold (LIDT) of the films is greatly influenced by the porosity, and the larger the porosity, the higher the LIDT of TiO2 films, with a value up to 16.7 J/cm2. However, the LIDT of SiO2 film is not improved compared with that without PEG, and when the PEG mass fraction increased from 0.8% to 8%, the LIDT of SiO2 film increased by 1.9 J/cm2. In summary, improving the porosity helps to improve the laser damage resistance of the film.

    Keywords
    Tools

    Get Citation

    Copy Citation Text

    Shaobin SUN, Junqi XU, Junhong SU, Yang LI, Tong WANG, Zheng LIU. Influence of PEG content on optical band gap and laser damage characteristics of porous films[J]. Journal of Applied Optics, 2024, 45(4): 841

    Download Citation

    EndNote(RIS)BibTexPlain Text
    Save article for my favorites
    Paper Information

    Category: Research Articles

    Received: Jul. 3, 2023

    Accepted: --

    Published Online: Oct. 21, 2024

    The Author Email: XU Junqi (徐均琪)

    DOI:10.5768/JAO202445.0407002

    Topics